ROCKWELL HARDNESS TESTER

Rockwell and Rockwell superficial:

SERIE RSD

Rockwell hardness tester 330RSD
Rockwell hardness tester 206RSD2

AUTOMATIC HARDENSS TESTERS FOR FAST USE

Rockwell hardness testers RSD series: Automatic, simple and very fast hardness tester HRC HRB HRA and other scales, with test loads from 3 to 250 kgf. Rockwell or Superficial Rockwell and Brinell HBWT. Conform to ASTM E10 – E18 – E103 / ISO 6506 – 6508 standards.

Test loads

From 3 to 187,5 kgf (From 29,42 to 1839 N) – As optional 250 kgf (2452 N)

Rockwell and superficial Rockwell ISO 6508 / ASTM E-18

HRA – HRB – HRC – HRD – HRF – HRG – HRL – HRM – HRR  /  HRN – HRT

Brinell HBWT ASTM E-103 / SO 6506

HB 30 – HB 10 – HB 5 – HB 2,5 – MPa (F/D2)

Vickers ISO 6507 / ASTM E-92 (Indentation only)

HV3 – HV10 – HV15 – HV30 – HV60 – HV100

RSD Rockwell Hardness tester

ONE DRIVE MEASUREMENTS

Rockwell hardness testers RSD are extremely accurate system with automatic preloading, loading and measurements. RSD AFFRI System hardness testers achieve the highest level of depth accuracy and measurement resolution available for Rockwell tests. Thanks to the AFFRI System, the real indentation measurement is guaranteed without any external interference in any condition.

  1. Auto-contact with the specimen
  2. Automatic clamping and activation of the reference surface point
  3. Auto preloading and loading
  4. Automatic measure
  5. Auto-return stroke when releasing the lever

The entire test cycle is complete and the result appears on the display.

Only 3″ for one hardness test!
(more with standardized dwell time)

Rockwell hardness test automatic

AUTO-CONTACT AND TEST ACTIVATION

Rockwell hardness tester clamp

Rockwell hardness testers RSD measuring head is equipped with a vertical sliding stroke of 50 mm / 2” including automatic contact with test surface.

The stroke also allows easy and fast tests on pieces with different thicknesses without acting on the tester head or the elevating screw.

When testing unstable samples or deflecting parts, the AFFRI System will follow the sample without losing contact thanks to its 50 mm stroke for indenter and clamping hood.

Accurate measurements on the first test, even in extreme conditions, will eliminate the need for repeated tests. The R&R data is at the top of its class.

CLAMPING TO THE LIMIT

Secure contact with the specimen is always maintained, even in the unlikely event of any specimen movement during the operation cycle. The clamping system blocks the specimen before the measurement cycle, it moves with the head for the whole measuring stroke generating a constant pressure. The clamping system assures perfect stability of any test piece throughout the test cycle.

  1. Perfect stability of any test piece throughout the test cycle
  2. Safe testing on oiled, rusty or dirty samples
  3. No more need for pedestals or additional support for the specimen
  4. The indenter is protected and retracted minimizing the risk of accidental damages.
  5. Test long bars, tubes or rings in just few seconds
Rockwell hardness tester steel

The clamping works automatically when pulling the lever! 
It can’t be easier than this!

INCREDIBLE AFFRI PERFORMANCE

Rockwell Hardness Tester RSD repeatability

Chances are you will never meet a similar test condition (as shown left) with a foam support under your test piece. At Affri we test each instrument under extreme conditions to assure the accuracy of every test.

The top surface referencing design minimizes errors caused by anvil ling problems associated with dirt or scale. This reduces sample preparation time and increases both accuracy and speed.

Absolute accuracy is assured even at the first indentation test. The constant clamping surface assures the right measurement with no need to repeat the test. The first result is correct and ABSOLUTE!

FAST AND EASY!

ROCKWELL HARDNESS TESTERS RSD SERIE

OTHER FEATURES

Rockwell hardness tester capacity

INFINITE CAPACITY

700 mm of vertical stroke or more. The moving tester’s head permits easy measurements on large pieces, reaching points at the top of the sample that would be difficult to be measured with common testers.

Rockwell hardness tester RSD base

OPEN SPACE

The wide working base is capable of bearing masses beyond 2000 kg which allows for steady hardness measurements on bulky or irregular pieces. It also offers a comfortable working base for small pieces.

Rockwell hardness tester wheel

CUSTOM BASES

Optional interchangeable base for hardness testing on external ring shape tubes, cylindrical surfaces and various samples diameter. Made by AFFRI, the tester stand can be designed for every special needs.

THE MODELS

Rockwell hardness tester 903RSD

903 RSD

Height capacity 700mm
Working base 330 x 390mm
Depth capacity 190mm

Rockwell hardness tester 330RSD

330 RSD

Height capacity 300mm
Working base 330 x 390mm
Depth capacity 190mm

Rockwell hardness tester 206RSD2

206 RSD

Height capacity 215mm
Depth capacity 190mm

portable Rockwell hardness tester

PORTABLE RSDMAG

ASTM E10 / E18
ISO 6506 / 6508

THE ACCESSORIES

INDENTERS

ASTM – ISO

TEST BLOCKS

ASTM – ISO

ANVILS

Standard and custom

TECHNICAL SPECIFICATIONS

StandardsEN-ISO 6508-2 / EN-ISO 6507-2 / EN-ISO 6506-2 / EN-ISO 2039 / EN-ISO 868 / ASTM E-18 / ASTM E-10 / ASTM E-103 / ASTM E-92 / ASTM E-2240 / JIS
Indenter and clamping-hood strokeAutomatic 0/50 mm
PreloadRSD: 98.1 N (10 kgf)
RS-SD: 29.4 N (3 kgf)
Force rangeRSD:
Rockwell: 588.4 - 980.7 - 1471 N (60 - 100 - 150 kgf)
Vickers (Indentation only): 98.07 - 980.7 N (10 - 100 kgf)
Brinell (On request): 98.07 - 612.9 - 1226 - 1839 N - On request 2452 N (10 - 62.5 - 125 - 187.5 kgf - On request 250 kgf)

RS-SD:
Superficial Rockwell: 147.1 - 294.2 - 441.3 N (15 - 30 - 45 kgf)
Vickers (Indentation only): 29.42 - 294.2 N (3 - 30)
Brinell (On request): 153.2 - 294.2 - 306.5 N (15.6 - 30 - 31.2 kgf)
Feasible testsRSD:
Rockwell: HRC - HRA - HRB - HRD - HRE - HRF - HRG - HRH - HRK - HRL - HRM - HRR
Vickers (Only indentation): HV10 - HV100
Brinell (On request): HB30 - HB10 - HB5 MPa (F/D2)

RS-SD:
Superficial Rockwell: HRN - HRT
Vickers (Only indentation): HV3 - HV30
Brinell (On request): HB30 - HB10 - HB5 MPa (F/D2)
Load accuracyBetter than 0.5%

FEATURED ROCKWELL HARDNESS TESTERS

Rockwell automatic hardness test

DAKOMASTER 300

Rockwell
Fully automatic hardness testing machine with test loads from 1 to 250 kgf. Rockwell, Superficial Rockwell and Brinell HBWT. Touchscreen PC and high level software.
See more
Rockwell automatic hardness test

MRS Serie

Rockwell
Fully automatic hardness testing machine with test loads from 1 to 250 kgf. Rockwell, Superficial Rockwell and Brinell HBWT. Different frames and supports.
See more
Rockwell automatic hardness instrument

DRM / EX / RT

Rockwell
Semi-automatic very simple hardness testing machines with test loads from 3 to 250 kgf. Rockwell, Superficial Rockwell and Brinell HBWT. Suitable for small samples.
See more
hardness tester RSD MAG_1

RSDMAG

Portable, Brinell, Rockwell
Portable hardness testing machine with test loads from 3 to 187,5 kgf. Rockwell, Superficial Rockwell and Brinell HBWT. Conform to ASTM E18 E10 and ISO…
See more
rockwell hardness tester prs - affri hardness testers

PRS

Rockwell, Tailored
High-speed automatic hardness tester for independent use of the measuring head in the production department and lines. Rockwell – Superficial Rockwell – Brinell/ Test loads…
See more
hardness tester Explorer

EXPLORER

Rockwell, Tailored
Automatic hardness tester connectable to robots and CNC machines. Rockwell – Superficial Rockwell – Brinell/ Test loads from 3 to 187,5 kgf (29,45 to 1839…
See more
Menu